New lithium-nickel-manganese multiple oxide and its manufacturing method

新規なリチウム・ニッケル・マンガン複合酸化物およびその製造方法

Abstract

PROBLEM TO BE SOLVED: To provide a positive electrode active material for a lithium ion secondary battery having a high charge and discharge capacity, excellent rate characteristics, and excellent cycle characteristics. SOLUTION: A lithium-nickel-manganese multiple oxide having a composition of Li x Ni y Mn z O 2 (wherein x is 1+1/9±(1+1/9)/10; y is 4/9±(4/9)/10; and z is 4/9±(4/9)/10), and preferably having a general formula of Li[Ni 0.5-0.5X Mn 0.5-0.5X Li X ]O 2 (wherein X is 0.05≤X≤0.11) and belonging to a crystal structure of monoclinic system and a space group of C12/ml(No.12) is used as the positive electrode material. The lithium-nickel-manganese multiple oxide having a peak intensity ratio I (002) /I (13-3) of ≥1.35, which is determined by the powder X-ray diffraction using Cu-Kα line by attributing the multiple oxide to a monoclinic C12/ml(No.12) crystal where the peak intensities of (002) plane and (13-3) plane in Miller indices hkl are measured, is preferable. COPYRIGHT: (C)2005,JPO&NCIPI
【課題】高い放電容量とレート特性およびサイクル特性に優れた、リチウムイオン二次電池用の正極活物質を提供する。 【解決手段】リチウムーニッケルーマンガン複合酸化物で、その組成がLi x Ni y Mn z O 2 でxが1+1/9±(1+1/9)/10,yが4/9±(4/9)/10,zが4/9±(4/9)/10であり、特に一般式Li[Ni 0.5−0.5X Mn 0.5−0.5X Li X ]O 2 で表した場合にXが0.05≦X≦0.11で、結晶構造が単斜晶系に属し、空間群がC12/m1(No.12)であるリチウム−ニッケル−マンガン複合酸化物を正極物質として用いる。リチウムーニッケルーマンガン複合酸化物としては、単斜晶系のC12/m1(No.12)で帰属した場合のミラー指数hklにおける(002)面及び(13−3)面でのCu−Kα線を用いた粉末X線回折のピーク強度比I (002) /I (13−3) が1.35以上であることが好ましい。 【選択図】 選択図なし。

Claims

Description

Topics

Download Full PDF Version (Non-Commercial Use)

Patent Citations (0)

    Publication numberPublication dateAssigneeTitle

NO-Patent Citations (0)

    Title

Cited By (30)

    Publication numberPublication dateAssigneeTitle
    CN-102659184-ASeptember 12, 2012奇瑞汽车股份有限公司Solid solution material and preparation method thereof as well as lithium ion battery containing material
    JP-2006107845-AApril 20, 2006Sumitomo Metal Mining Co Ltd, 住友金属鉱山株式会社非水系電解質二次電池用正極活物質およびこれを用いた非水系電解質二次電池およびその製造方法
    JP-2006117517-AMay 11, 2006Ishihara Sangyo Kaisha Ltd, 石原産業株式会社リチウム・遷移金属複合酸化物の製造方法及び該リチウム・遷移金属複合酸化物を用いてなるリチウム電池
    JP-2006172753-AJune 29, 2006Mitsubishi Chemicals Corp, 三菱化学株式会社リチウム二次電池正極材料用リチウムニッケルマンガン系複合酸化物粉体及びその製造方法、並びにそれを用いたリチウム二次電池用正極及びリチウム二次電池
    JP-2007123255-AMay 17, 2007Ishihara Sangyo Kaisha Ltd, 石原産業株式会社リチウム・遷移金属複合酸化物及びその製造方法並びにそれを用いてなるリチウム電池
    JP-2007273106-AOctober 18, 2007Matsushita Electric Ind Co Ltd, Sumitomo Metal Mining Co Ltd, 住友金属鉱山株式会社, 松下電器産業株式会社Positive electrode active material for nonaqueous electrolyte secondary battery, and nonaqueous electrolyte secondary battery using the same
    JP-2007273108-AOctober 18, 2007Matsushita Electric Ind Co Ltd, Sumitomo Metal Mining Co Ltd, 住友金属鉱山株式会社, 松下電器産業株式会社非水電解質二次電池用の正極活物質、その製造方法及びそれを用いた非水電解質二次電池
    JP-2008098154-AApril 24, 2008Sumitomo Chemical Co Ltd, 住友化学株式会社Lithium composite metal oxide and nonaqueous electrolyte secondary battery
    JP-2009032655-AFebruary 12, 2009Sumitomo Chemical Co Ltd, 住友化学株式会社Lithium composite metal oxide
    JP-2009179545-AAugust 13, 2009Nippon Chem Ind Co Ltd, 日本化学工業株式会社Composite carbonate and method for producing the same
    JP-2010282982-ADecember 16, 2010Ishihara Sangyo Kaisha Ltd, 石原産業株式会社リチウム・遷移金属複合酸化物及びそれを用いてなるリチウム電池
    JP-2011105594-AJune 02, 2011Mitsubishi Chemicals Corp, 三菱化学株式会社Nickel-manganese-cobalt based complex oxide, laminar lithium-nickel-manganese-cobalt based complex oxide, positive electrode material for lithium secondary batteries, positive electrode using the material, and lithium secondary battery
    JP-2012151083-AAugust 09, 2012Gs Yuasa Corp, 株式会社GsユアサPositive electrode active material for nonaqueous electrolyte secondary battery, lithium-transition metal composite oxide, method for manufacturing positive electrode active material for nonaqueous electrolyte secondary battery, and nonaqueous electrolyte secondary battery
    JP-2012151084-AAugust 09, 2012Gs Yuasa Corp, 株式会社Gsユアサ非水電解質二次電池用正極活物質、リチウム遷移金属複合酸化物、非水電解質二次電池用正極活物質の製造方法、及び非水電解質二次電池
    JP-2012151085-AAugust 09, 2012Gs Yuasa Corp, 株式会社GsユアサPositive electrode active material for nonaqueous electrolyte secondary battery, lithium-transition metal composite oxide, method for manufacturing the positive electrode active material, and nonaqueous electrolyte secondary battery
    JP-2014007034-AJanuary 16, 2014Gs Yuasa Corp, 株式会社Gsユアサ, Toda Kogyo Corp, 戸田工業株式会社Active material for nonaqueous electrolyte secondary battery, electrode for nonaqueous electrolyte secondary battery, and nonaqueous electrolyte secondary battery
    JP-2014503942-AFebruary 13, 2014ビーエーエスエフ ソシエタス・ヨーロピアBasf Se遷移金属複合酸化物前駆体の製造方法
    JP-2016516267-AJune 02, 2016ナノ ワン マテリアルズ コーポレーション, ナノ ワン マテリアルズ コーポレーション電池用途の層状リチウム混合酸化物の微細粉体及び超微細粉体、並びにナノ粉体の工業生産に関する錯形成前駆体配合方法論
    JP-2016524576-AAugust 18, 2016ナノ ワン マテリアルズ コーポレーション, ナノ ワン マテリアルズ コーポレーション, テレシタ フレアンザ−クルバーグ, テレシタ フレアンザ−クルバーグ電池用途のリチウム金属酸化物の微細粉体及び超微細粉体、並びにナノ粉体の工業生産に関する錯形成前駆体配合方法論
    JP-4496150-B2July 07, 2010石原産業株式会社リチウム・遷移金属複合酸化物の製造方法及び該リチウム・遷移金属複合酸化物を用いてなるリチウム電池
    JP-4595475-B2December 08, 2010住友金属鉱山株式会社非水系電解質二次電池用正極活物質およびこれを用いた非水系電解質二次電池およびその製造方法
    JP-5460329-B2April 02, 2014Agcセイミケミカル株式会社リチウム二次電池正極活物質の原料用の遷移金属化合物造粒体の製造方法
    KR-101451441-B1October 15, 2014니폰 가가쿠 고교 가부시키가이샤복합 탄산염 및 그의 제조 방법
    US-8440353-B2May 14, 2013Sumitomo Chemical Company, LimitedLithium mixed metal oxide
    US-9178247-B2November 03, 2015Sumitomo Chemical Company, LimitedLithium composite metal oxide and nonaqueous electrolyte secondary battery
    US-9293236-B2March 22, 2016Semidonconductor Energy Laboratory Co., Ltd.Lithium—manganese composite oxide, secondary battery, and electric device
    US-9543055-B2January 10, 2017Gs Yuasa International Ltd.Positive active material for nonaqueous electrolyte secondary battery, method of manufacturing the positive active material, electrode for nonaqueous electrolyte secondary battery, nonaqueous electrolyte secondary battery and method of manufacturing the secondary battery
    WO-2008032754-A1March 20, 2008Sumitomo Chemical Company, LimitedLithium composite metal oxides and nonaqueous-electrolyte secondary cell
    WO-2009005164-A1January 08, 2009Sumitomo Chemical Company, Limitedリチウム複合金属酸化物
    WO-2009057777-A1May 07, 2009Agc Seimi Chemical Co., Ltd.リチウム二次電池正極活物質の原料用遷移金属化合物の造粒体粉末及びその製造方法